Preparation of Near-Spherical α‑Al₂O₃ Particles by Enhanced Precipitation of Gibbsite from Sodium Aluminate Solution Using Highly Dispersed Al₂O₃ as Seeds

The near-spherical α-Al₂O₃ particles (∼200 nm) were prepared for the first time through the precipitation of gibbsite from a supersaturated sodium aluminate solution, with the addition of an acidic solution containing highly dispersed nanosized Al₂O₃ seeds. The near-spherical α-Al₂O₃ were achieved by employing seeds at 1100 °C, with the initial nucleation temperature being only 900 °C, due to the highly homogeneous dispersion of the seeds into gibbsite formation by in situ growth that can effectively enhance the role of the seeds in the phase transition. Moreover, the precipitation rate of sodium aluminate solution was significantly accelerated by 17-fold. This acceleration was due to the slightly acidic solution breaking the stability of sodium aluminate solution through a neutralization reaction on the seed surface, leading to the rapid formation of gibbsite nuclei on the seed surface. Our findings provide a feasible approach for the fabrication of well-dispersed α-Al₂O₃ particles and make the industrial production of well-dispersed α-Al₂O₃ from sodium aluminate solution a commercial reality.