Cyclophosphazene-Based Hybrid Nanoporous Materials as Superior Metal-Free Adsorbents for Gas Sorption Applications

Cyclophosphazene-based inorganic–organic hybrid nanoporous materials (CHNMs) have been synthesized by a facile solvothermal method. The condensation of pyrrole with the reaction product of phosphonitrilic chloride trimer and 4-hydroxybenzaldehyde resulted in the formation of high-surface-area CHNMs. The maximum specific surface area (SA_BET) of 1328 m² g^–1 with hierarchical pore structures having micropores centered at 1.18 nm and mesopores in the range of 2.6–3.6 nm was estimated from the N₂ sorption analysis. Observation of high SA_BET could be attributed to the synergy effect exerted by the cyclophosphazene moiety owing to its three-dimensional paddle wheel structure. The metal-free adsorbent exhibited a high and reversible CO₂ uptake of 22.8 wt % at 273 K and 1 bar. The performance is on the higher side among the reported metal-free inorganic–organic hybrid nanoporous adsorbents. Moreover, the high H₂ uptake of 2.02 wt % at 77 K and 1 bar is an added advantage. The superior performance of the adsorbents for the gas sorption applications could be attributed to the combined effect of high SA_BET and hierarchical pore structure, which has made CHNMs good candidates for energy and environmental applications.