Prediction and Experimental Investigation
of the Polymorphic Lanthanum Fluoride Selenides LaFSe and La2F4Se
Posted on 24.11.2022 - 16:34
Lanthanum fluoride selenides (A-LaFSe, B-LaFSe and La2F4Se) have been synthesized through high-temperature experiments from an appropriate La/LaF3/Se mixture and characterized using single-crystal as well as powder X-ray diffractometry and UV/Vis diffuse reflectance spectroscopy. A-type LaFSe crystallizes in the tetragonal space group P4/nmm with a = 413.79(3) pm, c = 715.24(5) pm, and Z = 2 with the PbFCl-type structure; B-type LaFSe in the hexagonal space group P63/mmc with a = 421.602(2) pm, c = 818.163(7) pm, and Z = 2 with the CeHSe-type structure; and La2F4Se in the trigonal space group R3̅m with a = 417.86(2) pm, c = 2326.78(9) pm, and Z = 3 in the Ce2F4Se-type structure, respectively, in agreement with the earlier work. The experiments are complemented by crystal-structure predictions for LaFSe, which were performed using global optimization with empirical potentials and ab initio energy local minimizations. The results of the calculations concur with the experimentally observed structures and predict additional, so far unknown LaFSe polymorphs. The electronic properties were investigated both experimentally and theoretically, demonstrating the possibilities for band gap engineering in LaFSe.
CITE THIS COLLECTION
Buyer, Constantin; Grossholz, Hagen; Wolf, Sarah; Zagorac, Dejan; Zagorac, Jelena; Schön, J. Christian; et al. (2022): Crystal-Structure Prediction and Experimental Investigation of the Polymorphic Lanthanum Fluoride Selenides LaFSe and La2F4Se. ACS Publications. Collection. https://doi.org/10.1021/acs.cgd.2c00810
Select your citation style and then place your mouse over the citation text to select it.
Read the peer-reviewed publication
J. Christian Schön
trigonal space grouptetragonal space grouphexagonal space groupenergy local minimizationscharacterized using singleband gap engineeringab initio </experimentally observed structurestype lafse crystallizes4 </ sub2 </ sub4 /<type structuretype lafsez </r </p </nmm </mmc </c </structure predictionsstructure predictionray diffractometrypredict additionalpowder xexperimental investigationempirical potentialselectronic propertiesearlier workcalculations concur