Silicotungstate, a Potential Electron Transporting Layer for Low-Temperature Perovskite Solar Cells

Download (1.59 MB)
journal contribution
posted on 12.07.2017, 00:00 by Yoon Ho Choi, Hyun Bin Kim, In Seok Yang, Sang Do Sung, Young Sik Choi, Jeongho Kim, Wan In Lee
Thin films of a heteropolytungstate, lithium silicotungstate (Li4SiW12O40, termed Li-ST), prepared by a solution process at low temperature, were successfully applied as electron transporting layer (ETL) of planar-type perovskite solar cells (PSCs). Dense and uniform Li-ST films were prepared on FTO glass by depositing a thin Li-ST buffer layer, followed by coating of a main Li-ST layer. The film thickness was controlled by varying the number of coating cycles, consisting of spin-coating and thermal treatment at 150 °C. In particular, by employing 60 nm-thick Li-ST layer obtained by two cycles of coating, the fabricated CH3NH3PbI3 PSC device demonstrates the photovoltaic conversion efficiency (PCE) of 14.26% with JSC of 22.16 mA cm–2, VOC of 0.993 mV and FF of 64.81%. The obtained PCE is significantly higher than that of the PSC employing a TiO2 layer processed at the same temperature (PCE = 12.27%). Spectroscopic analyses by time-resolved photoluminescence and pulsed light-induced transient measurement of photocurrent indicate that the Li-ST layer collects electrons from CH3NH3PbI3 more efficiently and also exhibits longer electron lifetime than the TiO2 layer thermally treated at 150 °C. Thus, Li-ST is considered to be a promising ETL material that can be applied for the fabrication of flexible PSC devices.