Aminoalkanoic Acids as Alternatives to Mercaptoalkanoic Acids for the Linker-Assisted Attachment of Quantum Dots to TiO2
journal contributionposted on 19.08.2016, 00:00 by Natalia Rivera-González, Saurabh Chauhan, David F. Watson
Linear aminoalkanoic acids (AAAs) and mercaptoalkanoic acids (MAAs) were characterized as bifunctional ligands to tether CdSe QDs to nanocrystalline TiO2 thin films and to mediate excited-state electron transfer (ET) from the QDs to TiO2 nanoparticles. The adsorption of 12-aminododecanoic acid (ADA) and 12-mercaptododecanoic acid (ADA) to TiO2 followed the Langmuir adsorption isotherm. Surface adduct formation constants (Kad) were ∼104 M–1; saturation amounts of the ligands per projected surface area of TiO2 (Γ0) were ∼10–7 mol cm–2. Both Kad and Γ0 differed by 20% or less for the two linkers. CdSe QDs adhered to ADA- and MDA-functionalized TiO2 films; data were well modeled by the Langmuir adsorption isotherm and Langmuir kinetics. For ADA- and MDA-mediated assembly values of Kad were (1.8 ± 0.4) × 106 and (2.4 ± 0.4) × 106 M–1, values of Γ0 were (1.6 ± 0.3) × 10–9 and (1.2 ± 0.1) × 10–9 mol cm–2, and rate constants were (14 ± 5) and (60 ± 20) M–1 s–1, respectively. Thus, the thermodynamics and kinetics of linker-assisted assembly were slightly more favorable for MDA than for ADA. Steady-state and time-resolved emission spectroscopy revealed that electrons were transferred from both band-edge and surface states of CdSe QDs to TiO2 with rate constants (ket) of ∼107 s–1. ET was approximately twice as fast through thiol-bearing linker 4-mercaptobutyric acid (MBA) as through amine-bearing linker 4-aminobutyric acid (ABA). Photoexcited QDs transferred holes to adsorbed MBA. In contrast, ABA did not scavenge photogenerated holes from CdSe QDs, which maximized the separation of charges following ET. Additionally, ABA shifted electron-trapping surface states to higher energies, minimizing the loss of potential energy of electrons prior to ET. These trade-offs involving the kinetics and thermodynamics of linker-assisted assembly; the driving force, rate constant, and efficiency of ET; and the extent of photoinduced charge separation can inform the selection bifunctional ligands to tether QDs to surfaces.
Read the peer-reviewed publication
kineticrate constantstime-resolved emission spectroscopytether CdSe QDsMAACdSe QDsTiO 2 Linear aminoalkanoic acidsnanocrystalline TiO 2TiO 2 nanoparticlesMDA-mediated assembly valuesETselection bifunctional ligandselectron-trapping surface statesexcited-state electron transferlinker-assisted assemblythiol-bearing linker 4- mercaptobutyric acidSurface adduct formation constantsADAscavenge photogenerated holesphotoinduced charge separationLangmuir adsorption isothermAAAK adTiO 2MBA12- aminododecanoic acidMDA-functionalized TiO 2 filmsABAamine-bearing linker 4- aminobutyric acid12- mercaptododecanoic acidΓ 0