Revealing the Active Phase of Copper during the Electroreduction of CO2 in Aqueous Electrolyte by Correlating In Situ X‑ray Spectroscopy and In Situ Electron Microscopy
journal contributionposted on 03.06.2020 by Juan-Jesus Velasco-Velez, Rik V. Mom, Luis-Ernesto Sandoval-Diaz, Lorenz J. Falling, Cheng-Hao Chuang, Dunfeng Gao, Travis E. Jones, Qingjun Zhu, Rosa Arrigo, Beatriz Roldan Cuenya, Axel Knop-Gericke, Thomas Lunkenbein, Robert Schlögl
Any type of content formally published in an academic journal, usually following a peer-review process.
The variation in the morphology and electronic structure of copper during the electroreduction of CO2 into valuable hydrocarbons and alcohols was revealed by combining in situ surface- and bulk-sensitive X-ray spectroscopies with electrochemical scanning electron microscopy. These experiments proved that the electrified interface surface and near-surface are dominated by reduced copper. The selectivity to the formation of the key C–C bond is enhanced at higher cathodic potentials as a consequence of increased copper metallicity. In addition, the reduction of the copper oxide electrode and oxygen loss in the lattice reconstructs the electrode to yield a rougher surface with more uncoordinated sites, which controls the dissociation barrier of water and CO2. Thus, according to these results, copper oxide species can only be stabilized kinetically under CO2 reduction reaction conditions.