Highly Active Oxygen Evolution on Carbon Fiber Paper Coated with Atomic-Layer-Deposited Cobalt Oxide

Download (681.57 kB)
journal contribution
posted on 25.02.2019 by Hyung Jong Choi, Gwon Deok Han, Kiho Bae, Joon Hyung Shim
In this work, we evaluated the oxygen evolution performance of cobalt oxide (CoOx)-coated carbon fiber paper in electrochemical water splitting. For a uniform coating of CoOx layers along the carbon fiber paper, the atomic layer deposition (ALD) technique was applied. We achieved a uniform and conformal coating of atomic-layer-deposited CoOx (ALD-CoOx) on the carbon fiber paper. The overpotential for oxygen evolution measured for the optimized ALD-coated carbon fiber paper was as low as 343 mV at 10 mA cm–2, which is competitive with the activity of state-of-the-art CoOx prepared on electrodes with large surface areas. Oxygen evolution is not enhanced after a critical thickness, about 28 nm in our study, is reached. The optimal thickness of the ALD-CoOx film is dependent on two competing effects: the high oxidation state of cobalt ions in thicker CoOx helps the oxygen evolution, whereas the introduction of a thick oxide coating decelerates the rate of charge transfer at the surface.

History

Exports