Chemiresistive Sensing of Ambient CO2 by an Autogenously Hydrated Cu3(hexaiminobenzene)2 Framework
journal contributionposted on 27.06.2019 by Ivo Stassen, Jin-Hu Dou, Christopher Hendon, Mircea Dincă
Any type of content formally published in an academic journal, usually following a peer-review process.
A growing demand for indoor atmosphere monitoring relies critically on the ability to reliably and quantitatively detect carbon dioxide. Widespread adoption of CO2 sensors requires vastly improved materials and approaches because selective sensing of CO2 under ambient conditions, where relative humidity (RH) and other atmosphere contaminants provide a complex scenario, is particularly challenging. This report describes an ambient CO2 chemiresistor platform based on nanoporous, electrically conducting two-dimensional metal–organic frameworks (2D MOFs). The CO2 chemiresistive sensitivity of 2D MOFs is attained through the incorporation of imino-semiquinonate moieties, i.e., well-defined N-heteroatom functionalization. The best performance is obtained with Cu3(hexaiminobenzene)2, Cu3HIB2, which shows selective and robust ambient CO2 sensing properties at practically relevant levels (400–2500 ppm). The observed ambient CO2 sensitivity is nearly RH-independent in the range 10–80% RH. Cu3HIB2 shows higher sensitivity over a broader RH range than any other known chemiresistor. Characterization of the CO2-MOF interaction through a combination of in situ optical spectroscopy and density functional theory calculations evidence autogenously generated hydrated adsorption sites and a charge trapping mechanism as responsible for the intriguing CO2 sensing properties of Cu3HIB2.