Framework Reduction and Alkali-Metal Doping of a Triply Catenating Metal−Organic Framework Enhances and Then Diminishes H2 Uptake
datasetposted on 06.01.2009, 00:00 authored by Karen L. Mulfort, Thea M. Wilson, Michael R. Wasielewski, Joseph T. Hupp
A permanently microporous metal−organic framework compound with the formula Zn2(NDC)2(diPyTz) (NDC = 2,6-naphthalenedicarboxylate, diPyTz = di-3,6-(4-pyridyl)-1,2,4,5-tetrazine) has been synthesized. The compound, which features a triply catenating, pillared-paddlewheel structure, was designed to be easily chemically reduced (diPyTz sites) by appropriate channel permeants. Reduction was achieved by using the naphthalenide anion, with the accompanying metal cation (Li+, Na+ or K+) serving to dope the compound in extraframework fashion. H2 uptake at 1 atm and 77 K increases from 1.12 wt % for the neutral material to 1.45, 1.60, and 1.51 wt % for the Li+-, Na+-, and K+-doped materials, respectively. The isosteric heats of adsorption are similar for all four versions of the material despite the large uptake enhancements for the reduced versions. Nitrogen isotherms were also measured in order to provide insight into the mechanisms of uptake enhancement. The primary mechanism is believed to be dopant-facilitated displacement of catenated frameworks by sorbed H2. More extensive cation doping decreases the H2 loading.
Read the peer-reviewed publication
diPyTz sitesuptake enhancementmaterialcompoundmetal cationuptake enhancementsNitrogen isothermsDiminishes H 2 UptakeAversioncatenated frameworkswtNaframework ReductionH 2.1 atmchannel permeantstriply catenatingNDC77 K increasescation doping decreasesLih 2 uptakemechanismnaphthalenide anionH 2 loadingextraframework fashion